SINELEC Conductive Compounds - PS
|
Compound Reference
|
Units
|
CCB2095
|
CCB1785
|
CCB2755
|
CCB2765
|
Test
Method
|
|
|
Mechanical
Properties
|
|||||||
|
Tensile Strength @ Yield
|
MPa |
35 |
22
|
20
|
20
|
ASTM D-638
|
|
|
Elongation @ break
|
%
|
19
|
15
|
23
|
10
|
ASTM
D-638
|
|
|
Notched Izod Impact @23°C
|
J/M
|
40
|
70
|
120
|
110
|
ASTM
D-256
|
|
|
Flexural Strength |
MPa
|
36
|
28
|
27
|
28
|
ASTM
D-790
|
|
|
Flexural Modulus |
MPa
|
2000
|
1700
|
1420
|
1500
|
ASTM
D-790
|
|
|
Mechanical
Properties - Heat Deflection Temp
|
|||||||
|
@0.46 MN/M2
|
°C
|
85
|
74
|
77
|
75
|
ASTM D648
|
|
|
Physical Properties |
|||||||
|
Specific gravity |
g/cc
|
1.1
|
1.1
|
1.05
|
1.10
|
ASTM D792
|
|
|
Melt Flow Index @ 200°C
/ 10KG
|
g/10min
|
1.5
|
1
|
1.6
|
5
|
ASTM D792
|
|
|
@200°C/21.6KG |
g/10
min
|
15.0
|
15
|
35
|
100.0
|
ASTM D1238
|
|
|
Shrinkage |
%
|
0.4-0.6
|
0.4-0.6
|
0.4-0.4-0.6
|
0.4-0.6
|
ASTM
D955
|
|
|
Electrical
Property
|
|||||||
|
Surface Resistivity |
Ohm
|
<1x105
|
<1x105
|
<1x105
|
<1x105
|
ASTM
D-257
|
|
|
Volume Resistivity |
Ohm-cm
|
<1x105
|
<1x105
|
<1x105
|
<1x105
|
ASTM
D-257
|
|
| Application | Injection Moulding | Profile Extrusion | Extrusion $ Injection Moulding | Sheet Extrusion for vacuum-forming, injection moulding | |||
Singapore Polymer Corporation Pte Ltd reserves the right to change its products any time. Data provided in this web publication may not always be updated. Information provided herein is for general information and is given in good faith. Specific technical information and directives must be obtained from our representatives before using our products, to determine the suitability for any particular use. No warranty is given nor is to be implied with respect to information given herein. Values presented are typical and intended to serve as guides only, and should not be considered as limits to the specifications. Freedom under patents, copyright and registered designs cannot be assumed.
Back
to SINELEC Conductive Compounds (Main Page)