SINPOLENE High/Medium-Gloss Polypropylene Compound |
|
|
SINPOLENE High/Medium-Gloss Polypropylene Compound |
|
SINPOLENE MFP is a series of polypropylene designed for injection molding of domestic appliances' housings where a high-gloss surface is necessary for high heat applications. All grades are mineral filled for good rigidity and dimensional stability while remaining food contact safe. The MFP grades are formulated for high heat applications.
|
PROPERTY
|
ASTM
METHOD
|
UNITS
|
MFP12EB3
|
MFP14UA3
|
MFP19EA3
|
| MECHANICAL | |||||
| Tensile Yield Strength |
D-638
|
MPa
|
35
|
25
|
36
|
| Elongation @ Break |
D-638
|
%
|
100
|
90
|
47
|
|
Flexural
Strength
|
D-790
|
MPa
|
47
|
42
|
47
|
|
Flexural
Modulus
|
D-790
|
MPa
|
2100
|
2700
|
2000
|
|
Notched Izod Impact Strength
@ 23°C
|
D-256
|
J/m
|
33
|
32
|
25
|
| THERMAL | |||||
|
Heat Distortion Temp (3.2mm)
|
D-648
|
||||
| @ 0.45MPa |
°C
|
135
|
127
|
127
|
|
| PHYSICAL | |||||
|
Specific
Gravity
|
D-792
|
-
|
0.98
|
1.69
|
0.98
|
|
Melt
Flow Index
|
D-1238
|
g/10min
|
23
|
20
|
14
|
|
Gloss
60°
|
D-523
|
GU
|
85
|
60
|
85
|
| PROCESSING | |||||
| Mold Shrinkage |
D-955
|
in/in
|
0.0180 - 0.0190
|
0.0110 - 0.0120
|
0.0130 - 0.0180
|
**The mould shrinkage values presented here are solely based on laboratory molded test bars. Users are strongly advised to conduct their own evaluation of tooling values as variable factors such as part thickness & configuration, and molding conditions could affect the part shrinkage.
Singapore Polymer Corporation Pte Ltd reserves the right to change its products any time. Data provided in this web publication may not always be updated. Information provided herein is for general information and is given in good faith. Specific technical information and directives must be obtained from our representatives before using our products, to determine the suitability for any particular use. No warranty is given nor is to be implied with respect to information given herein. Values presented are typical and intended to serve as guides only, and should not be considered as limits to the specifications. Freedom under patents, copyright and registered designs cannot be assumed.