SINPOLENE Calcium Carbonate Filled Polypropylene |
|
SINPOLENE REINFORCED PP COMPOUND
SINPOLENE CPP is a series of Calcium Carbonate filled homo and co-polymer polypropylene designed for injection molding. The difference in content and characteristics between the individual grades allows CPP series to meet the requirements for a wide range of applications, from speaker frames to tape reels in the manufacturing industry and furniture's to appliances' housings in domestic applications.
|
COMPOUND
REFERENCE
|
CPP
1020 |
CPP
1030 |
CPP
1040 |
CPP
1050 |
CPP
2020 |
CPP
2030 |
CPP
2040 |
||
|
PROPERTY
|
ASTM
METHOD
|
UNITS
|
-
|
||||||
| MECHANICAL | |||||||||
| Tensile Yield Strength |
D-638
|
MPa
|
32
|
30
|
28
|
27
|
27
|
25
|
24
|
| Flexural Strength |
D-790
|
MPa
|
43
|
44
|
45
|
45
|
28
|
30
|
32
|
| Flexural Modulus |
D-790
|
GPa
|
1.65
|
1.92
|
2.15
|
2.30
|
1.35
|
1.55
|
1.75
|
| Notched Izod Impact Strength @ 23 °C |
D-256
|
J/m
|
28
|
27
|
26
|
24
|
72
|
65
|
54
|
| THERMAL | |||||||||
| Heat Distortion Temp (3.2mm) |
D-648
|
°C
|
110
|
116
|
118
|
121
|
104
|
107 | 110 |
| Vicat Softening Point, 1 kg |
D-1525
|
°C
|
148
|
148
|
148
|
148
|
146
|
146 | 146 |
| PHYSICAL | |||||||||
| Specific Gravity |
D-792
|
g/cc
|
1.04
|
1.12
|
1.22
|
1.34
|
1.04
|
1.12
|
1.22
|
| Melt Flow Index |
D-1238
|
g/10min
|
10
|
10
|
6
|
8
|
10
|
10
|
9
|
| PROCESSING | |||||||||
| Mold Shrinkage** |
D-955
|
%
|
1.0-1.4
|
0.9-1.3
|
0.8-1.0
|
0.7-0.9
|
1.0-1.4
|
0.9-1.3 | 0.9-1.1 |
|
APPLICATIONS
|
Furniture, Appliances
Housings |
Appliances' base,
Speaker frames & boxes |
Furniture
|
Automotive and
Industrial Components |
|||||
**The mould shrinkage values presented here are solely based on laboratory molded test bars. Users are strongly advised to conduct their own evaluation of tooling values as variable factors such as part thickness & configuration, and molding conditions could affect the part shrinkage.
Singapore Polymer Corporation Pte Ltd reserves the right to change its products any time. Data provided in this web publication may not always be updated. Information provided herein is for general information and is given in good faith. Specific technical information and directives must be obtained from our representatives before using our products, to determine the suitability for any particular use. No warranty is given nor is to be implied with respect to information given herein. Values presented are typical and intended to serve as guides only, and should not be considered as limits to the specifications. Freedom under patents, copyright and registered designs cannot be assumed.